一、Q550CFC钢板尺寸、外形、重量及允许偏差

钢板的尺寸、外形、重量及允许偏差应符合GB/T709的规定。

经供需双方协议，也可供应其他尺寸、外形及允许偏差的钢板

N类偏差：正偏差负偏差相等

A类偏差：按公称厚度决定正偏差

B类偏差：固定负偏差为0.3

C类偏差：固定负偏差为0、按公称厚度决定正偏差

二、Q550CFC钢板执行标准：YB/T4137-2013.

三、Q550CFC钢板探伤：（Ⅰ、Ⅱ、Ⅲ级类探伤）

探伤：也叫超声波检验，是针对钢板内部重量的一种检验方法及手段，可以检验港版的内部缺陷。

根据需方要求，经供需双方协商，钢板可进行超声波检测，检测方法按GB/T2970或JB/T4730.3,检验方法和合格级别应在合同中注明。

四、

Q550CFC steel plate smelting process

Steel is smelted in a converter or an electric furnace and shall be refined outside the furnace;The delivery state of Q550CFC steel plate shall be thermomechanically controlled rolling (TMCP), TMCP+ tempering or quenching + tempering (quenching and tempering). The specific delivery state shall be agreed by both parties and indicated in the contract.Steel plates shall be delivered by cutting or flame cutting

Note: Tempering and quenching analysis

Tempering: To hold the steel plate at a certain appropriate temperature for a long time before cooling

Quenching: is to heat the steel plate after heat preservation in water oil or other inorganic salts and other media for rapid cooling

五、Q550CFC钢板化学成分

Q550CFC钢的化学成分（熔炼分析）应符合下表的规定（％）

Q550CFC化学成分要求

C

Si

Mn

P

S

Cr

Ni

Mo

V

Nb

Ti

B

≤0.09

≤0.5

≤2.0

≤0.02

≤0.01

≤0.8

≤1.8

≤0.7

≤0.1

≤0.12

≤0.05

≤0.005

六、Q550CFC钢板焊接裂纹敏感性指数（不大于）Pcm/%

钢牌号

产品厚度

名称

≤50

50-60

60-75

75-100

Q550CFC

0.25

0.25

0.28

0.30

七、Q550CFC钢板机械性能

Q550CFC的力学性能和工艺性能能应符合下表规定：

Q550CFC力学性能要求（适用于横向）

牌号

拉伸试验

弯曲试验

夏比V型冲击试验

上屈服强度

抗拉强度

断后伸长率

弯曲1800

温度

冲击吸收能量

厚度≤50

50-100

Q550CFC

550

530

670-830

16

d=3a

0

60

八、Q550CFC钢板冲击功